Product Name:Polyamide1010
We are a Polyamide 1010 (100%bio-based materials) manufacture, based in Zibo ,China, specialized in Polyamide Resin and Compounding with Annual Capacity of 20,000MT.
Polyamide 1010 is created through decanediamine and sebacic acid. Both elements are obtained from castor oil .It is almost 100% Bio-Based material, which can help you with reduce your CO2 footprint. The properties of PA1010 are between high performances polyamides such as PA12 and PA6 or PA6/6.
Special features
● 100 % Bio-Based Carbon Content (as a fraction of total organic carbon)
● Low water absorption and good dimensional stability
● Good chemical resistance
● Excellent mould ability
PRODUCT SPECIFICATIONS
Test Items |
Test methods |
Test Conditions |
Unit |
Typical Value |
Physical properties | ||||
Specific Gravity |
GB/T1033-1986 |
23℃ |
—— |
1.04 |
Shore Hardness |
GB/T2411-1980 |
—— |
D |
78 |
Melting range |
GB/T4608-1984 |
—— |
℃ |
200-210 |
Mechanical Properties | ||||
Tensile Strength |
GB/T1040-1992 |
50mm/min |
MPa |
60 |
Tensile Elongation |
GB/T1040-1992 |
50mm/min |
% |
≥50 |
Flexural Strength |
GB/T9341-2000 |
2mm/min |
MPa |
52 |
Impact Strength |
GB/T1043-1993 |
23℃ |
KJ/m2 |
N |
Impact Strength |
GB/T1043-1993 |
23℃ |
KJ/m2 |
6 |
Other | ||||
Water absorption |
GB/T 1034-1998 |
Saturation |
% |
2.1 |
Typical Processing Conditions Drying Temperature: 80-100 ℃
Drying Time: 4-8 h
Injection Temperature: 230-270 ℃
Extrusion Temperature: 220-260 ℃
Applications
PA1010 are mainly used in different lines or horses in auto products. It can also be used in cable surface coating, electronics and sports.